Refractory News

Effect of antioxidant addition types on the properties of magnesia carbon bricks

With the development of the economy, my country’s scrap steel resources are gradually increasing. It is expected that by 2030, my country’s scrap steel resources will increase from the current 200 million tons to 300 million tons. Under the guidance of national energy conservation and consumption reduction, the reuse of scrap steel resources is particularly […]

Effect of antioxidant addition types on the properties of magnesia carbon bricks Read More »

Main factors affecting the service life of the long nozzle and ways to improve it

Since the 21st century, with the enlargement of continuous casting equipment, the amount of steel passing through the shroud has gradually increased, from less than 1t/min to more than 7t/min at present. The increase in the amount of steel per unit time causes rapid erosion of the inner wall. Therefore, inner wall erosion has become

Main factors affecting the service life of the long nozzle and ways to improve it Read More »

How to make refractory fire brick

Step-by-Step Guide to Making Fire Bricks The manufacturing process of fire brick is similar to ordinary bricks. The usual steps are: 1.Digging2.Weathering3.Tempering4.Moulding5.Burning Fire bricks are produced from fire clay. The burnings are carried out in a superior type of kiln under carefully graduated temperature control. Processes of burning and cooling are kept rather slow.You can

How to make refractory fire brick Read More »

Causes, erosion process and loss mechanism of magnesia-carbon bricks lined with electric furnaces

1.Causes of corrosion of electric furnace lining during normal use During normal smelting, the furnace lining is in direct contact with high-temperature molten steel and slag, and the working conditions are very harsh. The reasons for furnace lining damage are: (1) Thermal spalling caused by arc radiation and chemical erosion at high temperatures. (2) The

Causes, erosion process and loss mechanism of magnesia-carbon bricks lined with electric furnaces Read More »

Application and development trend of raw materials for continuous casting functional refractories

Since the introduction of continuous casting technology in the 1950s, continuous casting functional refractories were also born. Accompanied by the progress of metallurgical technology, the expansion of steel, casting billet quality and service life extension, continuous casting functional refractories have also been developed significantly to improve the flow control, rectification and protection of the casting

Application and development trend of raw materials for continuous casting functional refractories Read More »